PVC (UPVC) injection

Application of stainless steel casting mold, chromium content of at least 13%, preferably 16%, at least 55 Rockwell hardness, hard chrome-plated steel mold can be processed to form a protective effect.
After production, the application of  titanium dioxide anatase a mild lye carefully cleaned and then sprayed mold surface quality oil spray or siliceous spray.
4, the melt temperature
Measure of available air-launched by 185-205 ℃ range. Smoothness of the material from the injection can know the exact upvc melt temperature. If the material in the injection after the rough, as evidenced by the material is not homogeneous (plastics insufficient), which  heat stabilizer for panel means that the temperature set too low; eg, injection newcomer bubble and smoke a lot of smoke, it means the temperature is too high.
5, the injection speed
Slower rate of fire, or cause excessive shear degradation of materials, the use of upvc produce extremely smooth, thick-walled products should be used multi-stage injection mold filling speed.
6, the screw speed
Should match the molding cycle may be. Screw Diethylene glycol dibenzoate  face velocity shall not exceed 0.15-0.2m / s
7, the back pressure
Up to 150bar, the lower the better, common to 5bar.
8, the retention time
At a temperature of 200 ℃, barrel residence time can not exceed five minutes. When the temperature is 210 ℃, cylinder residence time should not exceed 3 minutes.